Kiln Furniture

Kiln Furniture: KILN FURNITURE These are used for holding the material to be heated & to optimise the furnace loading . These have high thermal shock resistance , high Refractoriness under load, High Cold Crushing strength & repeated heating & cooling Cycles. At Hitemp we are manufacturing Mullite & Alumina Kiln Furniture. Mulite Refractories Properties Unit HWHF Max hot face temp Deg C 1700 Bulk Density g / cc 2.65 Apparent Porosity   17.5 Cold Crushing Strength Kg / cm2 1000 MOR at Room Temp 175 MOR at 1350 100 Reheat Change % at1450 deg / 6Hrs +/- 0.1 Thermal Conductivity % W / m deg K     At 800 deg 1.68   At 1000 deg 1.61   At 1200 deg 0.60 Chemical analysis AL2O3 Min   77.42   Sio2 Max  21.01   Fe2O3 Max 0.19

	Super Refractory Shapes
	Specifications Properties Unit 132 HB201 HB101 Max Hot Face Temp Deg C Max 1700 1750 1800 >Bulk Density g/cc Max 1.37 1.48 1.52 Apparent Porosity Min 50 45 45 Cold Crushing Strength Kg/cm2 Min 35 90 60 Reheat Change At 1450 deg / 24 Hrs Max +/-0.65 +0.65 at 1650 +0.41 Thermal Conductivity Maximum       W/mdeg K at 400 deg 0.28 0.70 1.60 1.60 At 600 deg 0.70 1.60 1.55 At 800 deg 0.55 1.50 1.30 At 1000 deg 0.65 1.30 1.30 At 1200 deg 0.70 1.30 1.30 Chemical Analysis Al2O3 Min 72 90 98 Sio2 Max 24 9 1 Fe2O3 Max 0.5 0.3 0.2
	Data is for general guidance only. Hitemp insulation refractories are meant for applications where high mechanical stability and insulating properties are required. Hitemp refractories are best suited for insulation of kilns and furnaces, both as hot face and back up linings. Hitemp refractories can be used for applications upto 1850 deg. The HB201, HB101bubble alumina range of insulating refractories is light weight, has good load bearing capacity and low heat capacity. They can be directly exposed to flame also.
	Wear Resistant Ceramics Coming Soon Grinding Media